CORROSION BEHAVIOR OF MMFX STEEL IN COMPARISON OF CONVENTIONAL REINFORCING STEEL
Hazem Mohamed Mohamed Moharram A;
Abstract
Corrosion, the cancer of steel, makes concrete deterioration as increasing of steel cross section occurred and longitudinal cracks appear after that decreasing of steel cross section occurs due to corrosion mechanism. All of above lead to weak interfacial
Other data
| Title | CORROSION BEHAVIOR OF MMFX STEEL IN COMPARISON OF CONVENTIONAL REINFORCING STEEL | Other Titles | دراسة قاتلية الصدأ للحديد MMFX تالوقار ةً تالحديد الوألوف | Authors | Hazem Mohamed Mohamed Moharram A | Keywords | CORROSION BEHAVIOR OF MMFX STEEL IN COMPARISON OF CONVENTIONAL REINFORCING STEEL | Issue Date | 2013 | Description | Corrosion, the cancer of steel, makes concrete deterioration as increasing of steel cross section occurred and longitudinal cracks appear after that decreasing of steel cross section occurs due to corrosion mechanism. All of above lead to weak interfacial |
Attached Files
| File | Size | Format | |
|---|---|---|---|
| 116610corrosion behavior of MMFX steel in comparison of conventional reinforcing steel.pdf | 632.45 kB | Adobe PDF | View/Open |
Similar Items from Core Recommender Database
Items in Ain Shams Scholar are protected by copyright, with all rights reserved, unless otherwise indicated.