Preparation and Characterization of Some Composites Based on Metals and Ceramics by Mechanical Alloying
Mohamed Abdel Aziz Taha Masoud;
Abstract
microstructure. The microhardness of the sintered Al2O3 - 0, 1, 5, 10
and 20 wt.% Cu composites milled at 20h were found 17.57, 16,89,
15.37, 14.22 and 12.59 GPa, respectively, whileas the fracture
toughness were 3.07, 3.46, 3.98, 4.56 and 4.89 %, respect
and 20 wt.% Cu composites milled at 20h were found 17.57, 16,89,
15.37, 14.22 and 12.59 GPa, respectively, whileas the fracture
toughness were 3.07, 3.46, 3.98, 4.56 and 4.89 %, respect
Other data
| Title | Preparation and Characterization of Some Composites Based on Metals and Ceramics by Mechanical Alloying | Other Titles | تحضير وتوصيف بعض المتراكبات المعتمده على المعادن والسيرامك بطريقة السبك الميكانيكى | Authors | Mohamed Abdel Aziz Taha Masoud | Keywords | Preparation and Characterization of Some Composites Based on Metals and Ceramics by Mechanical Alloying | Issue Date | 2013 | Description | microstructure. The microhardness of the sintered Al2O3 - 0, 1, 5, 10 and 20 wt.% Cu composites milled at 20h were found 17.57, 16,89, 15.37, 14.22 and 12.59 GPa, respectively, whileas the fracture toughness were 3.07, 3.46, 3.98, 4.56 and 4.89 %, respect |
Attached Files
| File | Size | Format | |
|---|---|---|---|
| 116912g280.pdf | 122.16 kB | Adobe PDF | View/Open |
Similar Items from Core Recommender Database
Items in Ain Shams Scholar are protected by copyright, with all rights reserved, unless otherwise indicated.