INFLUENCE OF HEAT TREATMENT CONDITIONS ON THE WEAR RESISTANCE AND HOT TENSILE PROPERTIES OF THE Ti-6Al-4V ALLOY
Manar Nady Abd EL-Ghany Mansour;
Abstract
In the current work, several heat treatments were carried out below and above the beta transus temperature of the Ti-6Al-4V alloy. The resultant microstructures and their effects on hardness, wear resistance and hot tensile properties of the Ti-6Al-4V alloy were examined. The results showed that solution treatment of Ti-6Al-4V samples followed by water quenching from β and α/β fields raised the alloy hardness from 380 to 575 and 656 HV respectively while no remarkable changes were observed after aging. Hot tensile strength of the as-forged sample increased from 671 to 756 MPa after water quenching from the β-phase field, while the air cooling decreased the tensile strength 644 MPa. The fracture mode of the tensile samples was more ductile in case of the solution treated samples compared to the as forged samples.
Other data
| Title | INFLUENCE OF HEAT TREATMENT CONDITIONS ON THE WEAR RESISTANCE AND HOT TENSILE PROPERTIES OF THE Ti-6Al-4V ALLOY | Other Titles | تأثير ظروف المعالجة الحرارية على مقاومة البرى و خصائص الشد على الساخن لسبيكة تيتانيوم-6 ألومنيوم- 4 فناديوم | Authors | Manar Nady Abd EL-Ghany Mansour | Issue Date | 2019 |
Recommend this item
Similar Items from Core Recommender Database
Items in Ain Shams Scholar are protected by copyright, with all rights reserved, unless otherwise indicated.